With the development of market economy, the technology of crystal drop molding is adopted for the breastplate, which makes the products gradually move towards technology, three-dimensional and high-grade, and improves the competitiveness of all kinds of products in the market. The production of crystal drop molding of breastplate consists of two kinds of glue, which we generally call AB glue. It is a modern surface decoration material, and its main component is polymer transparent resin, referred to as component A for short. Epoxy acrylic resin plus catalyst, referred to as component B, can be divided into soft crystal glue and hard crystal glue. Soft crystal adhesive (PU adhesive) is generally suitable for self-adhesive trademarks, PVC, pearl film and polyester materials. . . Soft plastic signs and hard crystal glue (also divided into UV crystal glue) are generally suitable for badges, trademarks, billboards, aluminum alloy badges, signs, badges, etc.

Production process:

1. First, lay the printed and cleaned items flat on the console, keep them horizontal, and wait for them to drip.

2. According to the dosage, take a cup, accurately weigh glue A (e.g. 90g), then weigh glue A and glue B (30g), and mix them evenly according to the ratio of 3: 1 (some crystal glue ingredients are 2: 1, others are1). ) 3. Take a clean syringe, suck the prepared glue into the syringe and drop it evenly on the surfaces such as signs and badges. Generally, the thickness of crystal glue layer is 2mm, so it can be leveled naturally.

4. After dropping crystal glue for 3-5 minutes, observe whether there are bubbles or dust particles on the rubber surface. If there are small bubbles, you can pick them off with a small needle. If you find that the dead corner is not smoothed with crystal glue, you can extradite them with a needle.

5. The poured name plate is cured at room temperature of 20℃-22℃ 10- 14 hours, and becomes a crystal plate with non-stick surface after hardening.

6. If it is an adhesive, trademark, etc. Its thickness is very thin and its boundary is not obvious. It is easy to cause crystal glue overflow when pouring, and it is difficult to reach the thickness of 2mm. Therefore, it is necessary to control the viscosity according to different conditions when making crystal glue, and 1-2 hours can be placed in the application process to improve the viscosity and adapt to the pouring of thin crystal glue.

7. Make a crystal glue name tag with a thickness of more than 2mm, which can be dripped twice. After the first drip, it will cure for 3-5 hours, and then drip another layer.

8. Cleaning after falling plastic (using toluene, xylene and cyclohexanone) The container needs to be cleaned. If the glue is insoluble in any solvent after hardening, it must be cleaned in machines and containers before hardening. The products made of crystal glue have the advantages of good visual effect, high transparency and high gloss, and should be widely used in screen printing industry. Note: If the weather is very cold, first heat the glue A and dilute it to about 15 degrees.